光伏镀膜玻璃
玻璃厚度∶ 1.6mm-3.2mm
常规厚度∶1.6mm/1.8mm/2.0mm/2.5mm/3.2mm
最大尺寸∶1350*2600mm
透光率∶ （3.2mm）≥93.5%
附着力∶ 用百格力
膜层硬度∶ ≥3 H
耐碱性∶在60℃过饱和的碱液中浸泡24小时后，透光率平均值衰减0.20%
耐酸性∶在2℃高浓度盐酸中浸泡24小时后，透光率平均值衰减0.20%
耐盐雾腐蚀性∶在盐雾试验机种放置96小时后，膜层无起泡，无剥落，无明显变色，透光率平均值衰减0.60%
耐恒温恒湿性∶在恒温恒湿箱中以温度85℃，温度85%的条件下放置100小时后，透光率平均值衰减0.50%
AR-Coating solar glass
Thickness: 1.6mm-3.2mm
Common Thickness:1.6mm/1.8mm/2.0mm/2.5mm/3.2mm
Max-size: 1350*2600mm
Transmittance: (3.2mm)≥93.5%
Adhesion: With Cross-Cut Tester
Film Hardness: ≥3H
Alkali Resistant: At 60℃ soaked saturated solution after 24 hours,the average transmittance attenuation 0.20%.
Acid Resistant: Soak 24 hours at25℃ high concentration of hydrochloric acid,light transmittance of 0.20% average attenuation.
Salt Spray: Placed for 96 hours in a salt spray test machine,film no blisters,no peeling off,no color,light transmittance of 0.60% average attenuation.
High Temperature&Humidity: In constant temperature and humidity box in the temperature of 85℃,85% humidity conditions for 1000 hours the average transmittance attenuation 0.50%.
玻璃厚度∶ 1.6mm-3.2mm
常规厚度∶1.6mm/1.8mm/2.0mm/2.5mm/3.2mm
最大尺寸∶1350*2600mm
透光率∶ （3.2mm）≥93.5%
附着力∶ 用百格力
膜层硬度∶ ≥3 H
耐碱性∶在60℃过饱和的碱液中浸泡24小时后，透光率平均值衰减0.20%
耐酸性∶在2℃高浓度盐酸中浸泡24小时后，透光率平均值衰减0.20%
耐盐雾腐蚀性∶在盐雾试验机种放置96小时后，膜层无起泡，无剥落，无明显变色，透光率平均值衰减0.60%
耐恒温恒湿性∶在恒温恒湿箱中以温度85℃，温度85%的条件下放置100小时后，透光率平均值衰减0.50%
AR-Coating solar glass
Thickness: 1.6mm-3.2mm
Common Thickness:1.6mm/1.8mm/2.0mm/2.5mm/3.2mm
Max-size: 1350*2600mm
Transmittance: (3.2mm)≥93.5%
Adhesion: With Cross-Cut Tester
Film Hardness: ≥3H
Alkali Resistant: At 60℃ soaked saturated solution after 24 hours,the average transmittance attenuation 0.20%.
Acid Resistant: Soak 24 hours at25℃ high concentration of hydrochloric acid,light transmittance of 0.20% average attenuation.
Salt Spray: Placed for 96 hours in a salt spray test machine,film no blisters,no peeling off,no color,light transmittance of 0.60% average attenuation.
High Temperature&Humidity: In constant temperature and humidity box in the temperature of 85℃,85% humidity conditions for 1000 hours the average transmittance attenuation 0.50%.